TiO2 derivatives with distinct morphologies have been successfully obtained by microwave assisted hydrothermal synthesis in acidic and alkaline medium using mild conditions. Titanium tetraisopropoxide (TTIP) was used as precursor in different environmental conditions under low temperatures, inferior to 150 °C, and short synthesis times, from 2 to 60 min. X ray diffraction (XRD), scanning electron microscopy (SEM), transmission electron microscopy (TEM) and N2 adsorption at 77 K (BET) were used to characterize the microstructural properties of the oxides. In the acidic synthesis the reaction time and temperature are not accompanied by significant changes in the structure of the material. However, in the basic conditions, the concentration of Na+ ions strongly influences the particle morphology and growth. The morphology of the nanoparticles shows irregular spheres in acidic conditions, while in alkaline medium, needle like structures are formed as well as aggregated nanotube-like structures synthesized in only 30 min. Besides the difference in the morphology and structure, in both systems, high surface area was obtained.

The performance of advanced electronic ceramics is directly related to the synthesis route employed. Sol-gel methods are widely used for this purpose. However, the physicochemical intermediate steps are still not well understood. Better understanding and control of these processes can improve the final quality of samples. In this work, we studied theoretically the formation of metal complexes between citric acid and lithium or barium metal cations with different citric acid/metal proportions, using Density Functional Theory electronic structure calculations. Infrared and Raman scattering spectra were simulated for the more stable geometric configurations. Using this methodology, we identified some features of complexes formed in the synthesis process. Our results show that the complexes can be distinguished by changes in the bands assigned to C=O, COH-, and COO- group vibrations. An estimate of the most stable complexes is made based on total energy.

Nitric oxide (NO) is a diffusible messenger that has been involved in numerous physiological processes ranging from vasodilatation and antimicrobial properties to wound healing. The beneficial effects can be attributed to the role NO plays in angiogenesis, inflammation and tissue remodeling. In the present work, a polymeric device for the sustained site specific delivery of nitric oxide using a latex rubber matrix from Hevea brasiliensis which encapsulates the spin trap iron(II)- diethyldithiocarbamate complex (FeDETC) was developed. The release profiles of NO from latex rubber matrix were studied and stability studies were carried out. Electron Paramagnetic Resonance (EPR) signal of NO was detected in the membrane exposed to ambient atmosphere at room temperature (25 °C) even after 350 hours. FTIR spectroscopy data indicated that NO-FeDETC retained its structural and spectroscopic properties upon encapsulation in the latex matrix. The NO delivery system developed in this work as a membrane, presented high stability.

Natural Rubber Latex (NRL) can be used successfully in controlled release drug delivery due to their excellent matrix forming properties. Recently, NRL has shown to stimulate angiogenesis, cellular adhesion and the formation of extracellular matrix, promoting the replacement and regeneration of tissue. A dermatological delivery system comprising a topically acceptable, inert support impregnated with a metronidazole (MET) solution was developed. MET 2-(2- methyl- 5-nitro- 1H- imidazol- 1-yl) ethanol, has been widely used for the treatment of protozoa and anaerobic bacterial infections. MET is a nitroimidazole anti-infective medication used mainly in the treatment of infections caused by susceptible organisms, particularly anaerobic bacteria and protozoa. In a previous study, we have tested NRL as an occlusive membrane for GBR with promising results. One possible way to decrease the inflammatory process, it was incorporated the MET in NRL. MET was incorporated into the NRL, by mixing it in solution for in vitro protein delivery experiments. The solutions of latex and MET were polymerized at different temperatures, from -100 to 40 °C, in order to control the membrane morphology. SEM microscopy analysis showed that the number, size and distribution of pores in NRL membranes varied depending on polymerization temperature, as well as its overall morphology. Results demonstrated that the best drug-delivery system was the membrane polymerized at -100 °C, which does release 77,1% of its MET content for up 310 hours.

In this work, we propose natural rubber latex (NRL) membranes as a protein delivery system. For this purpose Bovine Serum Albumin (BSA) was incorporated into the latex solution for in vitro protein delivery experiments. Different polymerization temperatures were used, from -10 to 27 °C, in order to control the membrane morphology. These membranes were characterized by Scanning Electron Microscopy (SEM), Atomic Force Microscopy (AFM), as well as the Lowry Method to measure the BSA release. SEM and AFM microscopy analysis showed that the number, size and distribution of pores in NRL membranes can be varied, as well as its overall morphology. We have found that the morphology of the membrane is the predominant factor for higher protein release, compared with pore size and number of pores. Results demonstrated that the best drug-delivery system was the membrane polymerized at RT (27 °C), which does release 66% of its BSA content for up to 18 days. Our results indicate that NRLb could be used in the future as an active membrane that could accelerate bone healing in GBR.